Click image to view full size image
Description：
, compared with 100Cr6 balls, appropriately increases Si, Mn element to improve its hardenability and elastic limit. The wear resistance is also better than 100Cr6. The applicable size range for the manufacture of rolling elements is larger than that of 100Cr6.
100CrMn6 chrome steel balls have a long life span and excellent performance. They are able to carry considerable loads, operate in a tough environment and mainly utilized in windmill bearing and other industrial motors, mechanisms, etc.
Specification:
100CrMn6 chrome steel balls | |
Diameters: |
2" (50.80mm)- 3" (76.20mm) |
Grade: |
G80-G500 |
Hardness: |
HRC60-66 |
Ultimate compressive strength |
2500 - 2600 MPa |
Temperature environment |
-60 - 150ºC |
Application: |
Windmill bearings, Industrial motors, etc. |
Equivalence of material:
100CrMn6 chrome steel balls | |
AISI/ASTM(USA) |
- |
VDEh (GER) |
100CrMn6 (1.3520) |
JIS (JAP) |
SUJ3 |
BS (UK) |
535A99 |
NF (France) |
100CM6 |
ГОСТ(Russia) |
SHKH15SG |
GB (China) |
Gcr15SiMn |
Chemical composition:
100CrMn6 chrome steel balls | |
C |
0.90% - 1.05% |
Si |
0.50% - 0.70% |
Mn |
1.00% - 1.20% |
P |
≤0.030% |
S |
≤0.025% |
Cr |
1.40% - 1.65% |
Ni |
≤0.30% |
Cu |
≤0.30% |
Our advantage:
● We have been engaged in steel ball production for more than 26 years;
● We offer a great variety of sizes ranged from 3.175mm to 38.1mm. The size spreadsheet can be referred as follows;
● We have a wide stock availability. Most of the standard sizes (3.175mm~38.1mm) and gauges (-8~+8) are available, which can be delivered immediately;
● Non-standard sizes and gauges can be manufactured under special request (such as 5.1mm, 5.15mm, 5.2mm, 5.3mm 5.4mm for seat track; 14.0mm for cam shaft and CV joint, etc.);
● Each batch of balls is inspected by sophisticated machines: roundness tester, roughness tester, metallographic analysis microscope, hardness tester (HRC and HV) to guarantee the quality.
http://www.hmmzsteelball.com/